7005 aluminium alloy

From Wikipedia, the free encyclopedia

7005 is an aluminium wrought alloy[1] used in bicycle frames , due to its relative ease of welding it does not require expensive heat treating - it is however harder to form making manufacture more challenging.[2] It has an Ultimate Tensile Strength of 350 MPa, a Fatigue Strength of 150 MPa and a density of 2.78 g/cm3.[3] It does not need to be precipitation hardened, but can be cooled in air.[4]

Specific forms of AL 7005 include[]

  1. 7005-O
  2. 7005-T5
  3. 7005-T53
  4. 7005-T6 [5]

Chemical composition[]

The alloy composition of 7005 is:[6]

7005 Aluminum alloy
No Element Percentage
1 Aluminium 91.0% - 94.7%
2 Chromium 0.06% - 0.20%
3 Copper <=0.10 %
4 Iron <=0.40 %
5 Magnesium 1.0% - 1.80%
6 Manganese 0.20% - 0.70%
7 Silicon <=0.35%
8 Titanium 0.010% - 0.060%
9 Zinc 4.0% - 5.0%
10 Zirconium 0.080% - 0.20%
11 Other, total <= 0.15%

Properties[]

No Property Value
1 Density 2.78 gm/cc
2 Elastic modulus [1] 70-80 GPa
3 Poisson Ratio[1] 0.33
4 Thermal conductivity[1] 166 W/mK
5 Ultimate Tensile Strength[1] 350 MPa
6 Fatigue Strength[1] 150 MPa

See also[]

  1. http://www.matweb.com/search/DataSheet.aspx?MatGUID=34c308934f7a4be589a80ecbee94406e&ckck=1
  2. http://www.matweb.com/search/datasheet.aspx?MatGUID=418587e416114026aae056b2695c5bde
  3. http://www.matweb.com/search/datasheet.aspx?MatGUID=0d7139f8ea0243cfbdbc53b68a75b906

References[]

  1. ^ a b c d e f "7005 aluminum alloy properties". 31 August 2012.
  2. ^ "Bicycle aluminum alloy".
  3. ^ "matweb Aluminium 7005".
  4. ^ Davis, Joseph R. (1993). Aluminum and Aluminum Alloys. ASM International. ISBN 9780871704962.
  5. ^ "Make it From". Make it From. Archived from the original on 2015-11-09.
  6. ^ "MatWeb - the Online Materials Information Resource". Archived from the original on 2014-04-27. Retrieved 2012-08-26.

Aluminum alloy table[]

Retrieved from ""