Arruda–Boyce model

Part of a series on
Continuum mechanics
${\displaystyle J=-D{\frac {d\varphi }{dx}}}$ Fick's laws of diffusion
Laws Conservations Mass Momentum Energy Inequalities Clausius–Duhem (entropy)
Solid mechanics Deformation Elasticity linear Plasticity Hooke's law Stress Finite strain Infinitesimal strain Compatibility Bending Contact mechanics frictional Material failure theory Fracture mechanics
Fluid mechanics Fluids Statics · Dynamics Archimedes' principle · Bernoulli's principle Navier–Stokes equations Poiseuille equation · Pascal's law Viscosity (Newtonian · non-Newtonian) Buoyancy · Mixing · Pressure Liquids Adhesion Capillary action Chromatography Cohesion (chemistry) Surface tension Gases Atmosphere Boyle's law Charles's law Combined gas law Fick's law Gay-Lussac's law Graham's law Plasma
Rheology Viscoelasticity Rheometry Rheometer Smart fluids Electrorheological Magnetorheological Ferrofluids
Scientists Bernoulli Boyle Cauchy Charles Euler Fick Gay-Lussac Graham Hooke Newton Navier Noll Pascal Stokes Truesdell
v t

In continuum mechanics, an Arruda–Boyce model^[1] is a hyperelastic constitutive model used to describe the mechanical behavior of rubber and other polymeric substances. This model is based on the statistical mechanics of a material with a cubic representative volume element containing eight chains along the diagonal directions. The material is assumed to be incompressible. The model is named after Ellen Arruda and Mary Cunningham Boyce, who published it in 1993.^[1]

The strain energy density function for the incompressible Arruda–Boyce model is given by^[2]

${\displaystyle W=Nk_{B}\theta {\sqrt {n}}\left[\beta \lambda _{\text{chain}}-{\sqrt {n}}\ln \left({\cfrac {\sinh \beta }{\beta }}\right)\right],}$

where ${\displaystyle n}$ is the number of chain segments, ${\displaystyle k_{B}}$ is the Boltzmann constant, ${\displaystyle \theta }$ is the temperature in kelvins, ${\displaystyle N}$ is the number of chains in the network of a cross-linked polymer,

${\displaystyle \lambda _{\mathrm {chain} }={\sqrt {\tfrac {I_{1}}{3}}},\quad \beta ={\mathcal {L}}^{-1}\left({\cfrac {\lambda _{\text{chain}}}{\sqrt {n}}}\right),}$

where ${\displaystyle I_{1}}$ is the first invariant of the left Cauchy–Green deformation tensor, and ${\displaystyle {\mathcal {L}}^{-1}(x)}$ is the inverse Langevin function which can be approximated by

${\displaystyle {\mathcal {L}}^{-1}(x)={\begin{cases}1.31\tan(1.59x)+0.91x&{\text{for}}\ |x|<0.841,\\{\tfrac {1}{\operatorname {sgn}(x)-x}}&{\text{for}}\ 0.841\leq |x|<1.\end{cases}}}$

For small deformations the Arruda–Boyce model reduces to the Gaussian network based neo-Hookean solid model. It can be shown^[3] that the Gent model is a simple and accurate approximation of the Arruda–Boyce model.

Alternative expressions for the Arruda–Boyce model[]

An alternative form of the Arruda–Boyce model, using the first five terms of the inverse Langevin function, is^[4]

${\displaystyle W=C_{1}\left[{\tfrac {1}{2}}(I_{1}-3)+{\tfrac {1}{20N}}(I_{1}^{2}-9)+{\tfrac {11}{1050N^{2}}}(I_{1}^{3}-27)+{\tfrac {19}{7000N^{3}}}(I_{1}^{4}-81)+{\tfrac {519}{673750N^{4}}}(I_{1}^{5}-243)\right]}$

where ${\displaystyle C_{1}}$ is a material constant. The quantity ${\displaystyle N}$ can also be interpreted as a measure of the limiting network stretch.

If ${\displaystyle \lambda _{m}}$ is the stretch at which the polymer chain network becomes locked, we can express the Arruda–Boyce strain energy density as

${\displaystyle W=C_{1}\left[{\tfrac {1}{2}}(I_{1}-3)+{\tfrac {1}{20\lambda _{m}^{2}}}(I_{1}^{2}-9)+{\tfrac {11}{1050\lambda _{m}^{4}}}(I_{1}^{3}-27)+{\tfrac {19}{7000\lambda _{m}^{6}}}(I_{1}^{4}-81)+{\tfrac {519}{673750\lambda _{m}^{8}}}(I_{1}^{5}-243)\right]}$

We may alternatively express the Arruda–Boyce model in the form

${\displaystyle W=C_{1}~\sum _{i=1}^{5}\alpha _{i}~\beta ^{2i-2}~(I_{1}^{i}-3^{i})}$

where ${\displaystyle \beta :={\tfrac {1}{N}}={\tfrac {1}{\lambda _{m}^{2}}}}$ and ${\displaystyle \alpha _{1}:={\tfrac {1}{2}}~;~~\alpha _{2}:={\tfrac {1}{20}}~;~~\alpha _{3}:={\tfrac {11}{1050}}~;~~\alpha _{4}:={\tfrac {19}{7000}}~;~~\alpha _{5}:={\tfrac {519}{673750}}.}$

If the rubber is compressible, a dependence on ${\displaystyle J=\det({\boldsymbol {F}})}$ can be introduced into the strain energy density; ${\displaystyle {\boldsymbol {F}}}$ being the deformation gradient. Several possibilities exist, among which the Kaliske–Rothert^[5] extension has been found to be reasonably accurate. With that extension, the Arruda-Boyce strain energy density function can be expressed as

${\displaystyle W=D_{1}\left({\tfrac {J^{2}-1}{2}}-\ln J\right)+C_{1}~\sum _{i=1}^{5}\alpha _{i}~\beta ^{i-1}~({\overline {I}}_{1}^{i}-3^{i})}$

where ${\displaystyle D_{1}}$ is a material constant and ${\displaystyle {\overline {I}}_{1}={I}_{1}J^{-2/3}}$ . For consistency with linear elasticity, we must have ${\displaystyle D_{1}={\tfrac {\kappa }{2}}}$ where ${\displaystyle \kappa }$ is the bulk modulus.

Consistency condition[]

For the incompressible Arruda–Boyce model to be consistent with linear elasticity, with ${\displaystyle \mu }$ as the shear modulus of the material, the following condition has to be satisfied:

${\displaystyle {\cfrac {\partial W}{\partial I_{1}}}{\biggr |}_{I_{1}=3}={\frac {\mu }{2}}\,.}$

From the Arruda–Boyce strain energy density function, we have,

${\displaystyle {\cfrac {\partial W}{\partial I_{1}}}=C_{1}~\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\,.}$

Therefore, at ${\displaystyle I_{1}=3}$,

${\displaystyle \mu =2C_{1}~\sum _{i=1}^{5}i\,\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\,.}$

Substituting in the values of ${\displaystyle \alpha _{i}}$ leads to the consistency condition

${\displaystyle \mu =C_{1}\left(1+{\tfrac {3}{5\lambda _{m}^{2}}}+{\tfrac {99}{175\lambda _{m}^{4}}}+{\tfrac {513}{875\lambda _{m}^{6}}}+{\tfrac {42039}{67375\lambda _{m}^{8}}}\right)\,.}$

Stress-deformation relations[]

The Cauchy stress for the incompressible Arruda–Boyce model is given by

${\displaystyle {\boldsymbol {\sigma }}=-p~{\boldsymbol {\mathit {1}}}+2~{\cfrac {\partial W}{\partial I_{1}}}~{\boldsymbol {B}}=-p~{\boldsymbol {\mathit {1}}}+2C_{1}~\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]{\boldsymbol {B}}}$

Uniaxial extension[]

Stress-strain curves under uniaxial extension for Arruda–Boyce model compared with various hyperelastic material models.

For uniaxial extension in the ${\displaystyle \mathbf {n} _{1}}$-direction, the principal stretches are ${\displaystyle \lambda _{1}=\lambda ,~\lambda _{2}=\lambda _{3}}$. From incompressibility ${\displaystyle \lambda _{1}~\lambda _{2}~\lambda _{3}=1}$. Hence ${\displaystyle \lambda _{2}^{2}=\lambda _{3}^{2}=1/\lambda }$. Therefore,

${\displaystyle I_{1}=\lambda _{1}^{2}+\lambda _{2}^{2}+\lambda _{3}^{2}=\lambda ^{2}+{\cfrac {2}{\lambda }}~.}$

The left Cauchy–Green deformation tensor can then be expressed as

${\displaystyle {\boldsymbol {B}}=\lambda ^{2}~\mathbf {n} _{1}\otimes \mathbf {n} _{1}+{\cfrac {1}{\lambda }}~(\mathbf {n} _{2}\otimes \mathbf {n} _{2}+\mathbf {n} _{3}\otimes \mathbf {n} _{3})~.}$

If the directions of the principal stretches are oriented with the coordinate basis vectors, we have

${\displaystyle {\begin{aligned}\sigma _{11}&=-p+2C_{1}\lambda ^{2}\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]\\\sigma _{22}&=-p+{\cfrac {2C_{1}}{\lambda }}\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]=\sigma _{33}~.\end{aligned}}}$

If ${\displaystyle \sigma _{22}=\sigma _{33}=0}$, we have

${\displaystyle p={\cfrac {2C_{1}}{\lambda }}\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]~.}$

Therefore,

${\displaystyle \sigma _{11}=2C_{1}\left(\lambda ^{2}-{\cfrac {1}{\lambda }}\right)\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]~.}$

The engineering strain is ${\displaystyle \lambda -1\,}$. The engineering stress is

${\displaystyle T_{11}=\sigma _{11}/\lambda =2C_{1}\left(\lambda -{\cfrac {1}{\lambda ^{2}}}\right)\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]~.}$

Equibiaxial extension[]

For equibiaxial extension in the ${\displaystyle \mathbf {n} _{1}}$ and ${\displaystyle \mathbf {n} _{2}}$ directions, the principal stretches are ${\displaystyle \lambda _{1}=\lambda _{2}=\lambda \,}$. From incompressibility ${\displaystyle \lambda _{1}~\lambda _{2}~\lambda _{3}=1}$. Hence ${\displaystyle \lambda _{3}=1/\lambda ^{2}\,}$. Therefore,

${\displaystyle I_{1}=\lambda _{1}^{2}+\lambda _{2}^{2}+\lambda _{3}^{2}=2~\lambda ^{2}+{\cfrac {1}{\lambda ^{4}}}~.}$

The left Cauchy–Green deformation tensor can then be expressed as

${\displaystyle {\boldsymbol {B}}=\lambda ^{2}~\mathbf {n} _{1}\otimes \mathbf {n} _{1}+\lambda ^{2}~\mathbf {n} _{2}\otimes \mathbf {n} _{2}+{\cfrac {1}{\lambda ^{4}}}~\mathbf {n} _{3}\otimes \mathbf {n} _{3}~.}$

If the directions of the principal stretches are oriented with the coordinate basis vectors, we have

${\displaystyle \sigma _{11}=2C_{1}\left(\lambda ^{2}-{\cfrac {1}{\lambda ^{4}}}\right)\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]=\sigma _{22}~.}$

The engineering strain is ${\displaystyle \lambda -1\,}$. The engineering stress is

${\displaystyle T_{11}={\cfrac {\sigma _{11}}{\lambda }}=2C_{1}\left(\lambda -{\cfrac {1}{\lambda ^{5}}}\right)\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]=T_{22}~.}$

Planar extension[]

Planar extension tests are carried out on thin specimens which are constrained from deforming in one direction. For planar extension in the ${\displaystyle \mathbf {n} _{1}}$ directions with the ${\displaystyle \mathbf {n} _{3}}$ direction constrained, the principal stretches are ${\displaystyle \lambda _{1}=\lambda ,~\lambda _{3}=1}$. From incompressibility ${\displaystyle \lambda _{1}~\lambda _{2}~\lambda _{3}=1}$. Hence ${\displaystyle \lambda _{2}=1/\lambda \,}$. Therefore,

${\displaystyle I_{1}=\lambda _{1}^{2}+\lambda _{2}^{2}+\lambda _{3}^{2}=\lambda ^{2}+{\cfrac {1}{\lambda ^{2}}}+1~.}$

The left Cauchy–Green deformation tensor can then be expressed as

${\displaystyle {\boldsymbol {B}}=\lambda ^{2}~\mathbf {n} _{1}\otimes \mathbf {n} _{1}+{\cfrac {1}{\lambda ^{2}}}~\mathbf {n} _{2}\otimes \mathbf {n} _{2}+\mathbf {n} _{3}\otimes \mathbf {n} _{3}~.}$

If the directions of the principal stretches are oriented with the coordinate basis vectors, we have

${\displaystyle \sigma _{11}=2C_{1}\left(\lambda ^{2}-{\cfrac {1}{\lambda ^{2}}}\right)\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]~;~~\sigma _{22}=0~;~~\sigma _{33}=2C_{1}\left(1-{\cfrac {1}{\lambda ^{2}}}\right)\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]~.}$

The engineering strain is ${\displaystyle \lambda -1\,}$. The engineering stress is

${\displaystyle T_{11}={\cfrac {\sigma _{11}}{\lambda }}=2C_{1}\left(\lambda -{\cfrac {1}{\lambda ^{3}}}\right)\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~I_{1}^{i-1}\right]~.}$

Simple shear[]

The deformation gradient for a simple shear deformation has the form^[6]

${\displaystyle {\boldsymbol {F}}={\boldsymbol {1}}+\gamma ~\mathbf {e} _{1}\otimes \mathbf {e} _{2}}$

where ${\displaystyle \mathbf {e} _{1},\mathbf {e} _{2}}$ are reference orthonormal basis vectors in the plane of deformation and the shear deformation is given by

${\displaystyle \gamma =\lambda -{\cfrac {1}{\lambda }}~;~~\lambda _{1}=\lambda ~;~~\lambda _{2}={\cfrac {1}{\lambda }}~;~~\lambda _{3}=1}$

In matrix form, the deformation gradient and the left Cauchy–Green deformation tensor may then be expressed as

${\displaystyle {\boldsymbol {F}}={\begin{bmatrix}1&\gamma &0\\0&1&0\\0&0&1\end{bmatrix}}~;~~{\boldsymbol {B}}={\boldsymbol {F}}\cdot {\boldsymbol {F}}^{T}={\begin{bmatrix}1+\gamma ^{2}&\gamma &0\\\gamma &1&0\\0&0&1\end{bmatrix}}}$

Therefore,

${\displaystyle I_{1}=\mathrm {tr} ({\boldsymbol {B}})=3+\gamma ^{2}}$

and the Cauchy stress is given by

${\displaystyle {\boldsymbol {\sigma }}=-p~{\boldsymbol {\mathit {1}}}+2C_{1}\left[\sum _{i=1}^{5}i~\alpha _{i}~\beta ^{i-1}~(3+\gamma ^{2})^{i-1}\right]~{\boldsymbol {B}}}$

Statistical mechanics of polymer deformation[]

The Arruda–Boyce model is based on the statistical mechanics of polymer chains. In this approach, each macromolecule is described as a chain of ${\displaystyle N}$ segments, each of length ${\displaystyle l}$. If we assume that the initial configuration of a chain can be described by a random walk, then the initial chain length is

${\displaystyle r_{0}=l{\sqrt {N}}}$

If we assume that one end of the chain is at the origin, then the probability that a block of size ${\displaystyle dx_{1}dx_{2}dx_{3}}$ around the origin will contain the other end of the chain, ${\displaystyle (x_{1},x_{2},x_{3})}$, assuming a Gaussian probability density function, is

${\displaystyle p(x_{1},x_{2},x_{3})={\cfrac {b^{3}}{\pi ^{3/2}}}~\exp[-b^{2}(x_{1}^{2}+x_{2}^{2}+x_{3}^{2})]~;~~b:={\sqrt {\cfrac {3}{2Nl^{2}}}}}$

The configurational entropy of a single chain from is

${\displaystyle s=c-k_{B}b^{2}r^{2}}$

where ${\displaystyle c}$ is a constant. The total entropy in a network of ${\displaystyle n}$ chains is therefore

${\displaystyle \Delta S=-{\tfrac {1}{2}}nk_{B}(\lambda _{1}^{2}+\lambda _{2}^{2}+\lambda _{3}^{2}-3)=-{\tfrac {1}{2}}nk_{B}(I_{1}-3)}$

where an affine deformation has been assumed. Therefore the strain energy of the deformed network is

${\displaystyle W=-\theta \,dS={\tfrac {1}{2}}nk_{B}\theta (I_{1}-3)}$

where ${\displaystyle \theta }$ is the temperature.

Notes and references[]

See also[]

• Hyperelastic material
• Rubber elasticity
• Finite strain theory
• Continuum mechanics
• Strain energy density function
• Neo-Hookean solid
• Mooney–Rivlin solid
• Yeoh (hyperelastic model)
• Gent (hyperelastic model)